| According to EN 10025-2 Thickness: < 3 mm ; yield strength: > 185 MPa |
| According to EN 10025-2 Thickness: < 3 mm ; tensile strength: 310 - 540 MPa |
| According to EN 10025-2 Thickness: 3 - 16 mm ; yield strength: > 185 MPa |
| According to EN 10025-2 Thickness: 3 - 16 mm ; yield strength: 290 - 510 MPa |
| According to EN 10025-2 Thickness: 16 - 40 mm ; yield strength: > 175 MPa |
| According to EN 10025-2 Thickness: 16 - 40 mm ; yield strength: 290 - 510 MPa |
| According to EN 10025-2 Thickness: 40 - 63 mm ; yield strength: > 175 MPa |
| According to EN 10025-2 Thickness: 40 - 63 mm ; yield strength: 290 - 510 MPa |
| According to EN 10025-2 Thickness: 63 - 80 mm ; yield strength: > 175 MPa |
| According to EN 10025-2 Thickness: 63 - 80 mm ; tensile strength: 290 - 510 MPa |
| According to EN 10025-2 Thickness: 80 - 100 mm ; yield strength: > 175 MPa |
| According to EN 10025-2 Thickness: 80 - 100 mm ; tensile strength: 290 - 510 MPa |
| According to EN 10025-2 Thickness: 100 - 150 mm ; yield strength: > 165 MPa |
| According to EN 10025-2 Thickness: 100 - 150 mm ; yield strength: 280 - 500 MPa |
| According to EN 10025-2 Thickness: 150 - 200 mm ; yield strength: > 155 MPa |
| According to EN 10025-2 Thickness: 150 - 200 mm ; tensile strength: 270 - 490 MPa |
| According to EN 10025-2 Thickness: 200 - 250 mm ; yield strength: > 145 MPa |
| According to EN 10025-2 Thickness: 200 - 250 mm ; tensile strength: 270 - 490 MPa |
| According to EN 10025-2 Longitudinal samples Thickness: < 1 mm ; elongation: > 10 % |
| According to EN 10025-2 Longitudinal samples Thickness: > 1.5 mm ; elongation: > 11 % |
| According to EN 10025-2 Longitudinal samples Thickness: 1.5 - 2.0 mm ; elongation: > 12 % |
| According to EN 10025-2 Longitudinal samples Thickness: 2.0 - 2.5 mm ; elongation: > 13 % |
| According to EN 10025-2 Longitudinal samples Thickness: 2.5 - 3.0 mm ; elongation: > 14 % |
| According to EN 10025-2 Longitudinal samples Thickness: 3 - 40 mm ; elongation: > 18 % |
| According to EN 10025-2 Longitudinal samples Thickness: 40 - 63 mm ; elongation: > 17 % |
| According to EN 10025-2 Longitudinal samples Thickness: 63 - 100 mm ; elongation: > 16 % |
| According to EN 10025-2 Longitudinal samples Thickness: 100 - 150 mm ; elongation: > 15 % |
| According to EN 10025-2 Longitudinal samples Thickness: 150 - 250 mm ; elongation: > 15 % |
| According to EN 10025-2 Tangential samples Thickness: < 1 mm ; elongation: > 8 % |
| According to EN 10025-2 Tangential samples Thickness: > 1.5 mm ; elongation: > 9 % |
| According to EN 10025-2 Tangential samples Thickness: 1.5 - 2.0 mm ; elongation: > 10 % |
| According to EN 10025-2 Tangential samples Thickness: 2.0 - 2.5 mm ; elongation: > 11 % |
| According to EN 10025-2 Tangential samples Thickness: 2.5 - 3.0 mm ; elongation: > 12 % |
| According to EN 10025-2 Tangential samples Thickness: 3 - 40 mm ; elongation: > 16 % |
| According to EN 10025-2 Tangential samples Thickness: 40 - 63 mm ; elongation: > 15 % |
| According to EN 10025-2 Tangential samples Thickness: 63 - 100 mm ; elongation: > 14 % |
| According to EN 10025-2 Tangential samples Thickness: 100 - 150 mm ; elongation: > 13 % |
| According to EN 10025-2 Tangential samples Thickness: 150 - 250 mm ; elongation: > 13 % |
| Density: 7.85 g / cm3 |