1.0214 (QST 36-3)
Einstufung
| Land |
Abschnitt |
Kategorie |
| Deutschland |
Unlegierte Stähle |
Andere Baustähle (nicht für Wärmebehandlung mit Rm <500 MPa bestimmt) |
Chemische Zusammensetzung
| Standard |
Fe, % |
Si, % |
Mn, % |
Al, % |
P, % |
C, % |
S, % |
|---|
| EN 10263-2 |
99.17–99.6 |
< 0.1 |
0.3–0.5 |
0.02–0.06 |
< 0.025 |
0.08–0.12 |
< 0.025 |
Informationen zum Lieferanten
Mechanische Eigenschaften bei 20 °C
| Rollen |
Standard |
Größe, mm |
dieSpannung |
Klassifizierer |
$$R_{m}$$, $$MPa$$ |
$$\psi$$, % |
Verarbeitung |
|---|
|
|
|
|
|
360–470 |
60–72 |
|
Properties
| Property |
|---|
| According to EN 10263-2 +U or +U+PE tensile strength: < 430 MPa |
| According to EN 10263-2 +U or +U+PE Relative contraction: > 60 % |
| According to EN 10263-2 +or AC +AC+PE tensile strength: < 380 MPa |
| According to EN 10263-2 +or AC +AC+PE Relative contraction: > 70 % |
| According to EN 10263-2 +U+C Diameter: 5 - 10mm ; tensile strength: < 520 MPa |
| According to EN 10263-2 +U+C Diameter: 5 - 10mm ; Relative narrowing: > 58 % |
| According to EN 10263-2 +U+C Diameter: 10 - 40 mm ; yield strength: < 510 MPa |
| According to EN 10263-2 +U+C Diameter: 10 - 40 mm ; the Relative narrowing: > 58 % |
| According to EN 10263-2 +U+C+AC Diameter: 2 - 5mm ; tensile strength: < 370 MPa |
| According to EN 10263-2 +U+C+AC Diameter: 2 - 5mm ; the Relative narrowing: > 72 % |
| According to EN 10263-2 +U+C+AC Diameter: 5 - 40 mm ; yield strength: < 360 MPa |
| According to EN 10263-2 +U+C+AC Diameter: 5 - 40 mm ; the Relative narrowing: > 72 % |
| According to EN 10263-2 +U+C+AC+LC Diameter: 2 - 5mm ; tensile strength: < 410 MPa |
| According to EN 10263-2 +U+C+AC+LC Diameter: 2 - 5mm ; the Relative narrowing: > 68 % |
| According to EN 10263-2 +U+C+AC+LC Diameter: 5 - 40 mm ; yield strength: < 400 MPa |
| According to EN 10263-2 +U+C+AC+LC Diameter: 5 - 40 mm ; the Relative narrowing: > 68 % |
| According to EN 10263-2 +AC+C Diameter: 5 - 10mm ; tensile strength: < 470 MPa |
| According to EN 10263-2 +AC+C Diameter: 5 - 10mm ; Relative narrowing: > 63 % |
| According to EN 10263-2 +AC+C Diameter: 10 - 40 mm ; yield strength: < 460 MPa |
| According to EN 10263-2 +AC+C Diameter: 10 - 40 mm ; the Relative narrowing: > 63 % |
| Density: 7.85 g/cm3 |
Analoga
| Deutschland |
USA |
GUS, Russland, Ukraine |
|---|
| D 10-2 |
SAE 1010 |
C10D |
Standards
Beschreibung der chemischen Elemente
| Element |
Maßeinheiten |
Beschreibung |
| Fe |
% |
Eisen |
| Si |
% |
Silizium |
| Mn |
% |
Mangan |
| Al |
% |
Aluminium |
| P |
% |
Phosphor |
| C |
% |
Kohlenstoff |
| S |
% |
Schwefel |
Beschreibung der mechanischen Eigenschaften
| Parameter |
Maßeinheiten |
Beschreibung |
| $$R_{m}$$ |
$$MPa$$ |
Zugfestigkeit |
| $$\psi$$ |
% |
Zusammenziehung |