Einstufung
| Land |
Abschnitt |
Kategorie |
| GUS, Russland, Ukraine |
Korrosionsbeständige Legierungen und Stähle |
Korrosionsbeständige Legierungen |
Chemische Zusammensetzung
| Standard |
Fe, % |
Si, % |
Mn, % |
Cr, % |
Ni, % |
Ce, % |
P, % |
C, % |
S, % |
Nb, % |
Mo, % |
W, % |
|---|
| TU 14-3-1093-82 |
17.445–91.07 |
< 0.6 |
1.2–2 |
20–22 |
44–48 |
< 0.05 |
< 0.02 |
0.03–0.07 |
< 0.015 |
0.9–1.3 |
4–5 |
2.8–3.5 |
Informationen zum Lieferanten
Properties
| Property |
|---|
| Pipes according to TU 14-3-1093-82 After austenization and stabilization Outer diameter: 13 - 60 mm; Wall thickness: 1.5 - 6.0 mm; Yield Strength:> 343 MPa |
| Pipes according to TU 14-3-1093-82 After austenization and stabilization Outer diameter: 13 - 60 mm; Wall thickness: 1.5 - 6.0 mm; Temporary resistance:> 686 MPa |
| Pipes according to TU 14-3-1093-82 After austenization and stabilization Outer diameter: 13 - 60 mm; Wall thickness: 1.5 - 6.0 mm; Elongation:> 30% |
| Calculated Properties Density: 8.64 g / cm3 |
Analoga
| Russland |
|---|
| 05ХН46МВБЧ ТУ 14-3-1093-82 |
Standards
Beschreibung der chemischen Elemente
| Element |
Maßeinheiten |
Beschreibung |
| Fe |
% |
Eisen |
| Si |
% |
Silizium |
| Mn |
% |
Mangan |
| Cr |
% |
Chrom |
| Ni |
% |
Nickel |
| Ce |
% |
Zer |
| P |
% |
Phosphor |
| C |
% |
Kohlenstoff |
| S |
% |
Schwefel |
| Nb |
% |
Niob |
| Mo |
% |
Molybdän |
| W |
% |
Wolfram |