EI415A-Sh (20XH3MVFA-Sh)
Einstufung
| Land |
Abschnitt |
Kategorie |
| GUS, Russland, Ukraine |
Korrosionsbeständige Legierungen und Stähle |
Korrosionsbeständige Legierungen |
Chemische Zusammensetzung
| Standard |
Fe, % |
Si, % |
Mn, % |
Cr, % |
Ni, % |
V, % |
P, % |
C, % |
S, % |
Mo, % |
W, % |
|---|
| OST 108.020.109-82 |
93.02–95.78 |
0.15–0.4 |
0.25–0.6 |
2.4–3.3 |
< 0.5 |
0.6–0.85 |
< 0.025 |
0.17–0.24 |
< 0.015 |
0.35–0.55 |
0.3–0.5 |
Informationen zum Lieferanten
Properties
| Property |
|---|
| Billets according to OST 108.961.05-80 / 87 VD Rotors Strength category KP60 Longitudinal samples Temporary resistance:> 736 MPa Elongation:> 13% |
| Billets according to OST 108.961.05-80 / 87 VD Rotors Strength category KP60 Longitudinal samples Impact strength KCU at 20 ° C:> 49 J / cm2 Relative narrowing:> 40% Conditional yield strength: 589 - 736 MPa |
| Billets according to OST 108.961.05-80 / 87 VD Rotors Strength category KP60 Tangential samples Test temperature 20 ° C Temporary resistance:> 716 MPa Elongation:> 11% Impact strength KCU at 20 ° C:> 39 J / cm2 |
| Billets according to OST 108.961.05-80 / 87 VD Rotors Strength category KP60 Tangential samples Test temperature 20 ° C Relative narrowing:> 32% Conditional yield strength: 589 - 736 MP |
| Billets according to OST 108.961.05-80 / 87 VD Rotors Strength category KP60 Tangential samples Test temperature 400 ° C Conditional yield strength:> 539 MPa |
| Billets according to OST 108.961.05-80 / 87 VD Rotors Strength category KP65 Tangential samples Test temperature 20 ° C Temporary resistance:> 736 MPa Elongation:> 11% Impact strength KCU at 20 ° C:> 39 J / cm2 |
| Billets according to OST 108.961.05-80 / 87 VD Rotors Strength category KP65 Tangential samples Test temperature 20 ° C Relative narrowing:> 32% Conditional yield strength: 615 - 765 MPa |
| Billets according to OST 108.961.05-80 / 87 VD Rotors Strength category KP65 Tangential samples Test temperature 400 ° C Conditional yield strength:> 549 MPa |
| Billets according to OST 108.961.05-80 / 87 VD Disks KP70 strength category Tangential samples Test temperature 20 ° C Temporary resistance:> 785 MPa Elongation:> 13% |
| Billets according to OST 108.961.05-80 / 87 VD Disks KP70 strength category Tangential samples Test temperature 20 ° C Impact strength KCU at 20 ° C:> 49 J / cm2 Relative narrowing:> 40% Yield strength: 647 - 795 MPa |
| Billets according to OST 108.961.05-80 / 87 VD Disks KP70 strength category Tangential samples Test temperature 550 ° C Conditional yield strength:> 392 MPa |
| Tests at elevated temperature According to OST 108.020.109-82 Temperature: 200 ° C; Yield Strength:> 542 MPa |
| Tests at elevated temperature According to OST 108.020.109-82 Temperature: 400 ° C; Yield Strength:> 473 MPa |
| Temperature: 500 ° C; Yield strength:> 443 MPa; Long-term tensile strength per 100,000 h: 207 - 266 MPa; Creep strength corresponding to 1% of the total deformation per 100,000 h: 118 - 167 MPa |
| Temperature: 550 ° C; Yield strength:> 394 MPa; Long-term tensile strength per 100,000 h: 148 - 158 MPa; Creep strength corresponding to 1% of the total deformation per 100,000 h: 89 - 108 MP |
| Tests at elevated temperature According to OST 108.020.109-82 Temperature: 600 ° C; Yield Strength:> 345 MPa |
| Calculated Properties Density: 7.87 g / cm3 |
Analoga
| Deutschland |
USA |
|---|
| 1.7707 |
K24065 |
Standards
Beschreibung der chemischen Elemente
| Element |
Maßeinheiten |
Beschreibung |
| Fe |
% |
Eisen |
| Si |
% |
Silizium |
| Mn |
% |
Mangan |
| Cr |
% |
Chrom |
| Ni |
% |
Nickel |
| V |
% |
Vanadium |
| P |
% |
Phosphor |
| C |
% |
Kohlenstoff |
| S |
% |
Schwefel |
| Mo |
% |
Molybdän |
| W |
% |
Wolfram |